Solder onto Boomslang Connector Pins
I've finished my boomslang, but had a hard time soldering onto the 48 pins of the connector. My solder seemed really sticky. Any recommendations on what type of solder to use next time? Mine didn't flow very well. Is flux needed? What diameter?
#3
Boost Czar
iTrader: (62)
Join Date: May 2005
Location: Chantilly, VA
Posts: 79,499
Total Cats: 4,080
I use the thinnest wire they have....the silver-resin stuff.
if you look here, you can see what sam means....
all the tips of those wires are tinned (or soldered solid). I do the same on the ends of the contacts of the 48pin connector. Then you simply lay the wire over top of the contact, press the iron tip one the wire, and the two will melt together.
if you look here, you can see what sam means....
all the tips of those wires are tinned (or soldered solid). I do the same on the ends of the contacts of the 48pin connector. Then you simply lay the wire over top of the contact, press the iron tip one the wire, and the two will melt together.
#4
Boost Pope
iTrader: (8)
Join Date: Sep 2005
Location: Chicago. (The less-murder part.)
Posts: 33,039
Total Cats: 6,604
I guess the question would be- what kind of solder did you use?
The best solder for general-purpose stuff like this, and the kind that I use for 99% of my work, is plain ole' 60/40 rosin-core. That's 60% tin, 40% lead, and a rosin flux built right in.
Problem is that it's getting harder to find. Thanks to our good friend the RoHS directive, a lot of solder nowadays is lead-free. Here in the US, lead-based solder still isn't prohibited, but it's getting harder to find as some manufacturers are discontinuing lead-based solder preemptively. The new stuff contains copper and silver, it has a much higher melting point, and it just doesn't seem to flow as smoothly. You can still buy lead-based solder, you just have to look for it. Radio Shack carries it as P/N 64-017 (0.5 oz, .032"), and 64-005 (2.5oz, .032"). Avoid the "clear flux" style and all the other gimmicky ones- you just want standard 60/40 rosin-core.
I do not generally find it necessary to use a seperate flux. Just make sure the part to be soldered is clean.
Some terminals have a plating on them that makes soldering difficult. In these situations, it helps to rough up the surface a bit with fine sandpaper or a dremel with an abrasive pad. Also, make sure to get the piece hot enough before ladeling on the solder. For soldering wires to heavy terminals, I'll pre-tin the stripped end of the wire and set it aside, then start heating up the terminal, first with just a small amount of solder to aid heat conduction off the tip, then with more solder once it starts to flow. Once the terminal is fully wetted, apply the wire and remove the iron.
Speaking of irons, a good one makes a difference. Cheap irons have cheap tips that tend to be conical in shape and oxidize rather rapidly. A good tip will have a flatted profile and be made from a material that does not oxidize. Weller, SunPro, and MetCal all make good irons- if possible, get one with a base that has a variable temperature control. Here's an example of a good iron: http://www.action-electronics.com/wewes51.htm Yes, it's $104, but it's the last iron you'll ever buy.
The best solder for general-purpose stuff like this, and the kind that I use for 99% of my work, is plain ole' 60/40 rosin-core. That's 60% tin, 40% lead, and a rosin flux built right in.
Problem is that it's getting harder to find. Thanks to our good friend the RoHS directive, a lot of solder nowadays is lead-free. Here in the US, lead-based solder still isn't prohibited, but it's getting harder to find as some manufacturers are discontinuing lead-based solder preemptively. The new stuff contains copper and silver, it has a much higher melting point, and it just doesn't seem to flow as smoothly. You can still buy lead-based solder, you just have to look for it. Radio Shack carries it as P/N 64-017 (0.5 oz, .032"), and 64-005 (2.5oz, .032"). Avoid the "clear flux" style and all the other gimmicky ones- you just want standard 60/40 rosin-core.
I do not generally find it necessary to use a seperate flux. Just make sure the part to be soldered is clean.
Some terminals have a plating on them that makes soldering difficult. In these situations, it helps to rough up the surface a bit with fine sandpaper or a dremel with an abrasive pad. Also, make sure to get the piece hot enough before ladeling on the solder. For soldering wires to heavy terminals, I'll pre-tin the stripped end of the wire and set it aside, then start heating up the terminal, first with just a small amount of solder to aid heat conduction off the tip, then with more solder once it starts to flow. Once the terminal is fully wetted, apply the wire and remove the iron.
Speaking of irons, a good one makes a difference. Cheap irons have cheap tips that tend to be conical in shape and oxidize rather rapidly. A good tip will have a flatted profile and be made from a material that does not oxidize. Weller, SunPro, and MetCal all make good irons- if possible, get one with a base that has a variable temperature control. Here's an example of a good iron: http://www.action-electronics.com/wewes51.htm Yes, it's $104, but it's the last iron you'll ever buy.
#7
Boost Pope
iTrader: (8)
Join Date: Sep 2005
Location: Chicago. (The less-murder part.)
Posts: 33,039
Total Cats: 6,604
Yeah, I thought it would be uncouth of me to suggest that the OP buy a Metcal MX-500, which is the one I use here at the office. They're a paltry $500 or so (plus tips). The Weller I linked to is the new version of the one I have at home, which is about 15 years old and still running flawlessly. I do love the Metcal, though. You can change tips in two seconds, and it only takes about ten seconds from turn-on for the tip to reach operating temperature.
#9
Elite Member
Thread Starter
iTrader: (6)
Join Date: Sep 2007
Location: CA
Posts: 2,016
Total Cats: 13
Is the strength of the solder to pin bond enough to keep it from breaking? Seems likely if it's even slightly bent, the solder will pop off the pin. It hasn't happened yet and I'm probably over thinking it.
#10
Boost Pope
iTrader: (8)
Join Date: Sep 2005
Location: Chicago. (The less-murder part.)
Posts: 33,039
Total Cats: 6,604
Impossible to say without knowing how good a job you did with it. If the solder flowed properly onto the pin, then you should be able to support the weight of the car with the joint.
#11
mkturbo.com
iTrader: (24)
Join Date: May 2006
Location: Charleston SC
Posts: 15,177
Total Cats: 1,681
Thats the soldering iron I use at work. It is some highend Pace model. I will get an exact model number tommorow, but all I can say is it is amazing. I used a cheap 8$ radio shack soldering iron to build my first MS back in Feb 2007. Now after using a good soldering iron I cant go back. We have the wellers that Joe posted above at work and even those dont cut it with me any more.